Titanium Anode For Sodium Hypochlorite Generator System

Titanium Anode for Sodium Hypochlorite Generator System

50.0 USD

Sodium Hypochlorite Generator Cell
Current Density:2000A/m2
Working life:2years
Application:Sodium Hypochlorite
Temperature:less than 60 degree.

Inquiry Now

Product Attribute

Min. Order 1 Piece/Pieces
Trade Term FOB,CFR,DDP,EXW
Payment Terms L/C, T/T, WU
Place of Origin Shaanxi, China (Mainland)
Means of Transport Ocean, Air, Land
Production Capacity 30pcs in 20days
Packing Plastic or paper as...
Delivery Date 2 days to 15 days...
Brand Name Taijin
Place of Origin: Shaanxi,China (Mainland)
Composition: Titanium ASTM B265 Gr1 or Gr2
Coating: Mixed Metal Oxide( Iridum base)
Coating uniformity: Greater than 90 percent
Application Sea Water treatment
Ti Content (%): 99%
Current output of soil: 100A/m2
Current output of sea: 600A/m2 SEA WATER
Shape: Sheet
Quality Control: ISO9001:2008,SGS,ect.

Product Description

 

TAIJIN Titanium Anode for Sodium Hypochlorite Generator

 

 

By electrolyzing sea water or salt water, sodium chloride in sea water or salt water is oxidized into hypochlorous acid sodium, and it can generate the hypochlorous acid by hydrolysis, then hypochlorous acid decomposes further to form new ecological oxygen, new ecological oxygen has strong oxidizing, they can make protein and other cells of bacteria and virus degeneration, thus kill pathogenic microbes, and effectively prevent microbial contamination.

 

  Application

Power plant cooling water antifouling, large vessel ballast water treatment, small hypochlorous acid sodium generator, life sewage treatment etc.

²  Specification and performance

All the products are customized as client's request.

Specification

Unit

Parameter

Ruthnium

G/m2

≥6.0

Chlorine   evolution potential

(Vs.SCE)/V

≤1.13

Polarizability

/m   V

≤40

Accelerated   life

h

≥120

Homogeneity

%

≤15

Working life

Y

≥5

 

a)    Temperature:0~40℃

b)    Concentration of electrolyte:30~50g/L

²  Substrate:

Titanium ASTMB265 Grade 1

Chemical Composition

N

C

H

O

Fe

Ti

other

Maximum Content

0.03%

0.08%

0.015%

0.18%

0.20%

99%

0.4%

²  Coating: Ruthenium base mixed coating, customized by client's request.

²  Current Efficiency Test:

Test   Conditions

Results

3.5% NaCl solution, current:1500A/m2,   temperature:15±1℃

>85%

²  Accelerated Life test:

Test   Conditions

Results

1mol/l H2SO4,   current:20000A/m2, temperature:40±1℃

>85%